Production techniques
The foundation for pottery figure painting is the image carrier, in other words, the vase onto which an image is painted. Popular shapes alternated with passing fashions. Whereas many recurred after intervals, others were replaced over time. But they all had a common method of manufacture: after the vase was made, it was first dried before being painted. The workshops were under the control of the potters, who as owners of businesses had an elevated social position.
The extent to which potters and painters were identical is uncertain. It is likely that many master potters themselves made their main contribution to the production process as vase painters while employing additional painters. It is, however, not easy to reconstruct links between potters and painters. In many cases, such as Telson and the Tleson Painter, Amasis and the Amasis Painter or even Nikosthenes and Painter N, it is impossible to make unambiguous attributions, although in much of the scientific literature these painters and potters are assumed to be the same person. But such attributions can only be made with confidence if the signatures of potter and painter are at hand.
The painters, who were either slaves or craftsmen paid as pottery painters, worked on unfired, leather-dry vases. In the case of black-figure production the subject was painted on the vase with a clay slurry (a slip, in older literature also designated as varnish) which turned black and glossy after firing. This was not "paint" in the usual sense, since this surface slip was made from the same clay material as the vase itself, only differing in the size of the component particles, achieved during refining the clay before potting began. The area for the figures was first painted with a brush-like implement. The internal outlines and structural details were incised into the slip so that the underlying clay could be seen through the scratches. Two other earth-based pigments giving red and white were used to add details such as ornaments, clothing or parts of clothing, hair, animal manes, parts of weapons and other equipment. White was also frequently used to represent women’s skin.
The success of all this effort could only be judged after a complicated, three-phase firing process that generated the red color of the body clay and the black of the applied slip. Specifically, the vessel was fired in a kiln at a temperature of about 800 °C, with the resultant oxidization turning the vase a reddish-orange color. The temperature was then raised to about 950 °C with the kiln's vents closed and greenwood added to remove the oxygen. The vessel then turned an overall black. The final stage required the vents to be re-opened to allow oxygen into the kiln, which was allowed to cool down. The vessel then returned to its reddish-orange color due to renewed oxidization, while the now-sintered painted layer remained the glossy black color that had been created in the second stage.
Although scoring is one of the main stylistic indicators, some pieces do without. For these, the form is technically similar to the orientalizing style, but the image repertoire no longer reflects orientalizing practice.
Developments
The evolution of black-figure pottery painting is traditionally described in terms of various regional styles and schools. Using Corinth as the hub, there were basic differences in the productions of the individual regions, even if they did influence each other. Especially in Attica, although not exclusively there, the best and most influential artists of their time characterized classical Greek pottery painting. The further development and quality of the vessels as image carriers are the subjects of this section.
Comments
Post a Comment